Ferroelectric-domain-controlled magnetic anisotropy in Co40Fe40B20/YMnO3 multiferroic heterostructure

 

J. W. Wang,1 Y. G. Zhao,1,a) C. Fan,2 X. F. Sun,2 S. Rizwan,3 S. Zhang,1 P. S. Li,1 Z. Lin,1 Y. J. Yang,4,5 W. S. Yan,4 Z. L. Luo,4 L. K. Zou,3 H. L. Liu,3 Q. P. Chen,1 X. Zhang,1 M. H. Zhu,1 H. Y. Zhang,1 J. W. Cai,3 X. F. Han,3 Z. H. Cheng,3 C. Gao,4,5 D. Xie,6 and T. L. Ren6

1Department of Physics and State Key Laboratory of Low-Dimensional Quantum Physics, Tsinghua University, Beijing 100084, China

2Hefei National Laboratory for Physical Sciences at the Microscale, University of Science and Technology of China, Hefei, Anhui 230026, China

3State Key Laboratory of Magnetism, Institute of Physics, Chinese Academy of Sciences, Beijing 100190, China

4National Synchrotron Radiation Laboratory & School of Nuclear Science and Technology, University of Science and Technology of China, Hefei, Anhui 230026, China

5CAS Key Laboratory of Materials for Energy Conversion, Department of Materials Science and Engineering, University of Science and Technology of China, Hefei, Anhui 230026, China